Abstract
A soluble poly(2-methoxy-5-decoxy)-p-phenylene vinylene (PMODOPV) was synthesized via dehydrochlorination reaction and characterized by UV-visible absorption spectrum. The results showed that PMODOPV had a broad optical absorption band in the range of 450---550 nm and the optical band gap was calculated to be around 2.12 eV. The third-order nonlinear optical susceptibilities (?(3)) of PMODOPV films implanted by 30-keV N+ ions in the dose range of 3.8 * 10^(15)---9.6 * 10^(16) ions/cm2 were measured by degenerate four-wave mixing (DFWM) technique. The results demonstrated that the resonant and off-resonant ?(3) values were all enhanced significantly by means of ion implantation. The maximum resonant ?(3) value of 9.67 * 10^(-9) esu at 532 nm and off-resonant ?(3) value of 2.49 * 10^(-10) esu at 1.064 ?m were obtained when the ion dose was 3.8 * 10^(16) ions/cm2.
© 2005 Chinese Optics Letters
PDF Article
More Like This
Cited By
You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an Optica member, or as an authorized user of your institution.
Contact your librarian or system administrator
or
Login to access Optica Member Subscription