Abstract
To investigate the thermal stability of Mo/Si multilayers with different initial crystallinities of Mo layers, two kinds of Mo/Si multilayers were deposited by DC magnetron sputtering and annealed at 300°C and 400°C. The period thickness compactions of multilayers with crystalized and quasi-amorphous Mo layers were 0.15 nm and 0.30 nm at 300°C, respectively, and the stronger the crystallinity, the lower the extreme ultraviolet reflectivity loss. At 400°C, the period thickness compactions of multilayers with crystalized and quasi-amorphous Mo layers were 1.25 nm and 1.04 nm, respectively. It was shown that multilayers with a crystalized Mo layer had better thermal stability at 300°C but were less stable at 400°C than multilayers with a quasi-amorphous Mo layer. These changes in stability at 300°C and 400°C were due to the significant transition of the crystalline structure. The transition of the crystal structure leads to increased surface roughness, more interdiffusion, and compound formation.
© 2023 Optica Publishing Group
Full Article | PDF ArticleMore Like This
Robert S. Rosen, Daniel G. Stearns, Michael A. Viliardos, Michael E. Kassner, Stephen P. Vernon, and Yuanda Cheng
Appl. Opt. 32(34) 6975-6980 (1993)
Ileana Nedelcu, Robbert W. E. van de Kruijs, Andrey E. Yakshin, and Fred Bijkerk
Appl. Opt. 48(2) 155-160 (2009)
V. V. Kondratenko, Yu. P. Pershin, O. V. Poltseva, A. I. Fedorenko, E. N. Zubarev, S. A. Yulin, I. V. Kozhevnikov, S. I. Sagitov, V. A. Chirkov, V. E. Levashov, and A. V. Vinogradov
Appl. Opt. 32(10) 1811-1816 (1993)