Abstract
A technology called self-aligned selective undercut dry etching processing has been demonstrated for fabricating a highly efficient hybrid optical spot size converter (SSC) on a Si-on-insulator (SOI) template. The process was based on a bonded wafer between the upper InP-based multiple quantum well heterostructure and the lower SOI substrate. After defining the mask on the upper InP-based ridge waveguide, ${{\rm CF}_4}/{{\rm O}_2}$ dry reactive ion etching was then used for selective undercut etching of the Si material from the surrounding materials, forming a vertical waveguide coupler of the optical SSC. The lower waveguide, whose dimension is even smaller than the upper one, can thus be vertically self-aligned to the top ridge via an independent processing step. A laterally tapered waveguide ranging from 0.3 to 3 µm in width on the upper InP waveguide was fabricated. The phase-matching condition of the vertical coupler leads to a length of 45 µm and extracts 88% conversion efficiency. The selective undercut etching processing in III-V/SOI material provides a vertical self-alignment scheme for realizing compact and submicron scale heterogeneous integration in a Si photonics template.
© 2020 Optical Society of America
Full Article | PDF ArticleMore Like This
Jing Pu, Kim Peng Lim, Doris Keh Ting Ng, Vivek Krishnamurthy, Chee Wei Lee, Kun Tang, Anthony Yew Seng Kay, Ter Hoe Loh, and Qian Wang
Opt. Lett. 40(7) 1378-1381 (2015)
Ying Xue, Yu Han, Yi Wang, Zunyue Zhang, Hon Ki Tsang, and Kei May Lau
Opt. Lett. 45(7) 1754-1757 (2020)
Zhongfa Liao, S. J. Wagner, M. Z. Alam, V. Tolstikhin, and J. Stewart Aitchison
Opt. Lett. 42(20) 4167-4170 (2017)