Abstract
The nominal composition of (A-Ce:YMASG) ceramic phosphors was fabricated by the vacuum sintering technique. The introduction of as a second phase partially enters the crystal lattice, which was confirmed by the composition changing of the samples through x-ray diffraction measurement. An impurity phase of was observed in Ce:YMASG and disappeared with the introduction of at the concentration of 10 wt. %. When the content of increased to 30 and 50 wt. %, the second phase of was measured with actual weight ratios of 7.72 and 20.55 wt. %, respectively. The third phase of was found with the further addition of at 70 wt. %; the weight ratios of Ce:YMASG, , and were 68.756, 18.457, and 12.787 wt. %, respectively. The luminescent characters of the samples were measured by the photoluminescence spectra and electroluminescent spectra. With the increase of from 0 to 30 wt. %, the emission wavelength of plummeted from 610 to 552 nm, and the luminous efficacy of the samples increased from 35 to 65 lm/W.
© 2019 Optical Society of America
Full Article | PDF ArticleMore Like This
Xiyue Zhang, Le Zhang, Chen Hou, Jian Kang, Yanbin Li, Bingheng Sun, Yang Li, and Hao Chen
Opt. Express 30(14) 25078-25092 (2022)
Jie Chen, Yanru Tang, Xuezhuan Yi, Yanna Tian, Gang Ao, Deming Hao, Yandan Lin, and Shengming Zhou
Opt. Mater. Express 9(8) 3333-3341 (2019)
Yan Ru Tang, Sheng Ming Zhou, Xue Zhuan Yi, Hui Lin, Shuai Zhang, and De Ming Hao
Opt. Lett. 40(23) 5479-5481 (2015)