Abstract

Strong infrared photoluminescence (PL) was observed for the first time from black Si (b-Si) formed by femtosecond laser irradiation and treated by rapid thermal annealing. The PL peak energy changes from 0.78 to 0.84 eV (1.59 to 1.48 μm) when increasing the annealing temperature from 500°C to 1200°C, showing a tunable property. Compared to those after annealing at 1000°C, both the peak intensity and the peak energy change slightly after annealing at higher temperatures of 1100°C and 1200°C, showing a high thermal stability of their structures and PL properties. With the x-ray photoelectron spectroscopy (XPS) results from the b-Si before and after etching in KOH solution, the PL is attributed to dislocation-related (D1) luminescence rather than sulfur-related impurity center luminescence. The integrated intensity of D1 PL as a function of excitation power can be fitted by IPm with m of 0.58, suggesting that the PL of the b-Si sample originates from the recombination of bound-to-bound states. The high thermal activation energy of 75.2 meV suggests a high quenching temperature of D1 PL, showing a potential of application at room temperature. This work may promote the progress of research on b-Si in the area of Si-based optoelectronics.

© 2013 Optical Society of America

Full Article  |  PDF Article
OSA Recommended Articles
Sub-bandgap photo-response of non-doped black-silicon fabricated by nanosecond laser irradiation

Chun-Hao Li, Ji-Hong Zhao, Qi-Dai Chen, Jing Feng, and Hong-Bo Sun
Opt. Lett. 43(8) 1710-1713 (2018)

Light emitting properties of Si+ self-ion implanted silicon-on-insulator from visible to infrared band

Lingxi Ouyang, Chong Wang, Xiaoxu Feng, Jie Yang, Mengwei Zhou, Feng Qiu, Rongfei Wang, and Yu Yang
Opt. Express 26(12) 15899-15907 (2018)

High photoluminescence quantum yields generated from N-Si-O bonding states in amorphous silicon oxynitride films

Pengzhan Zhang, Leng Zhang, Yaozheng Wu, Sake Wang, and Xuefeng Ge
Opt. Express 26(24) 31617-31625 (2018)

References

You do not have subscription access to this journal. Citation lists with outbound citation links are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access OSA Member Subscription

Cited By

You do not have subscription access to this journal. Cited by links are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access OSA Member Subscription

Figures (5)

You do not have subscription access to this journal. Figure files are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access OSA Member Subscription

Metrics

You do not have subscription access to this journal. Article level metrics are available to subscribers only. You may subscribe either as an OSA member, or as an authorized user of your institution.

Contact your librarian or system administrator
or
Login to access OSA Member Subscription