A single crystal was grown by the Czochralski process. Its thermal conductivity was measured by photothermal analysis and reached 8.1 and along and perpendicular to the axis, respectively. These values are in good agreement with the predicted ones. The optical spectroscopy of the crystal, such as its absorption and emission cross sections under the two polarizations, its fluorescence lifetime, and its laser parameters, is investigated. Cw laser oscillation is obtained for what is to our knowledge the first time in this material under titanium sapphire pumping at 984 nm. We obtain 420 mW of output power for a 2% output coupler at 1029 nm. With a thin sample, the laser wavelength decreases to 1015 nm. In this case the quantum defect is as small as 2.9%. The weak heat release of the material suggests good prospects for its use in high-power applications.
© 2004 Optical Society of AmericaFull Article | PDF Article
20 September 2017: A typographical correction was made to the author listing.
OSA Recommended Articles
V. E. Kisel, A. E. Troshin, N. A. Tolstik, V. G. Shcherbitsky, N. V. Kuleshov, V. N. Matrosov, T. A. Matrosova, and M. I. Kupchenko
Opt. Lett. 29(21) 2491-2493 (2004)
Junhai Liu, Huaijin Zhang, Xavier Mateos, Wenjuan Han, Valentin Petrov, and Jiyang Wang
Opt. Express 16(22) 17729-17734 (2008)
A. Lucca, M. Jacquemet, F. Druon, F. Balembois, P. Georges, P. Camy, J. L. Doualan, and R. Moncorgé
Opt. Lett. 29(16) 1879-1881 (2004)