Abstract

We demonstrate indium gallium nitride/gallium nitride/aluminum nitride (AlN/GaN/InGaN) multi-quantum-well (MQW) ultraviolet (UV) light-emitting diodes (LEDs) to improve light output power. Similar to conventional UV LEDs with AlGaN/InGaN MQWs, UV LEDs with AlN/GaN/InGaN MQWs have forward voltages (Vf’s) ranging from 3.21 V to 3.29 V at 350 mA. Each emission peak wavelength of AlN/GaN/InGaN MQW UV LEDs presents 350 mA output power greater than that of the corresponding emission peak wavelength of AlGaN/InGaN MQW UV LEDs. The light output power at 350mA of AlN/GaN/InGaN MQWs UV LEDs with 375 nm emission wavelength can reach around 26.7% light output power enhancement in magnitude compared to the AlGaN/InGaN MQWs UV LEDs with same emission wavelength. But 350mA light output power of AlN/GaN/InGaN MQWs UV LEDs with emission wavelength of 395nm could only have light output power enhancement of 2.43% in magnitude compared with the same emission wavelength AlGaN/InGaN MQWs UV LEDs. Moreover, AlN/GaN/InGaN MQWs present better InGaN thickness uniformity, well/barrier interface quality and less large size pits than AlGaN/InGaN MQWs, causing AlN/GaN/InGaN MQW UV LEDs to have less reverse leakage currents at −20 V. Furthermore, AlN/GaN/InGaN MQW UV LEDs have the 2-kV human body mode (HBM) electrostatic discharge (ESD) pass yield of 85%, which is 15% more than the 2-kV HBM ESD pass yield of AlGaN/InGaN MQW UV LEDs of 70%.

© 2015 Optical Society of America

1. Introduction

Gallium nitride (GaN)-based ultraviolet (UV) light-emitting diodes (LEDs) are gaining attention in fields such as UV photolithography, high-density optical data storage, water purification, and portable chemical/biological agent detection/analysis systems. A lattice-mismatched sapphire substrate with a GaN layer induces a high density of the threading dislocations (TDs) during GaN layer growth [1]. Some reports revealed that high TD densities degrade the output power of GaN-based UV LEDs [2,3]. The strong influence of TD on light output was proposed to be caused by reduced localization of minority carriers in quantum wells (QWs) rich in indium (In) and increased trapping at TDs or other nonradiative recombination centers [4]. For blue and green GaN-based LEDs, radiative efficiency is mainly related to the localized states originating from the phase separation or In fluctuation in the InGaN QW [5]. However, the UV LEDs have less localized states than blue and green LEDs because phase separations do not easily occur at low In content. The emission efficiency would be reduced without the assistance of the localized state in InGaN wells low in In of near-UV LEDs. In addition to weak carrier localization effect, the effects of low In content include a much lower potential barrier height of the InGaN/GaN QW in UV LEDs that leads to weak carrier confinement [6,7]. Consequently, the quantum efficiency of a UV LED is drastically decreased with a decrease in in content in the InGaN well. Replacing the InGaN barriers with aluminum (Al) GaN barriers significantly increases the band offset between QWs and barriers resulting in increased efficiency [8]. However, the large lattice mismatch between AlGaN barrier and InGaN QW can result in a large piezoelectric and spontaneous polarization field in the QW, thereby reducing the radiative recombination probability of LEDs. Aside from the AlGaN barrier of UV LEDs, the AlInGaN quaternary barrier has been widely used in short-wavelength UV LEDs because of the characteristics of tuning band, strain, and internal field in the wells [9–18]. Increase in the band offset for the UV LED MQWs enhances carrier confinement and then improves emission efficiency. AlN barrier can generate large band offset for the application of the UV LED MQWs. However, material combination with a big difference in lattice constants, like InGaN/AlN MQWs, has rarely been chosen for well and barrier layers. It would have large strain and thus strong piezoelectric field in each of the InGaN and AlN layers; moreover, growth conditions (e.g., temperature) of both materials are quite different, making it difficult to obtain good quality of heterostructure. Anazawa et al. have reported the strain-compensated AlN/InGaN MQWs [19]. InGaN layer would compress the GaN and AlN layers and tense GaN. Therefore, AlN/InGaN would have a strain-compensated multiheterostructure to GaN. However, the thickness of the each layer should be precisely controlled to have strain-compensated AlN/InGaN MQWs. The piezoelectric field would appear once we miss the prescribed thickness for each layer of the strain-compensated AlN/InGaN MQWs. Arif et al. have reported the staggered QW structure to deal with the internal field of the wells [20]. The staggered QW structure could improve the electron hole overlap in the QWs with internal field. Therefore, we would like to introduce UV LEDs with AlN/GaN/InGaN MQW structure to replace AlGaN/InGaN MQW of UV LEDs. The effects of the UV LEDs with AlN/GaN/InGaN MQW structure on the electrical and optical properties of the GaN-based UV LEDs, as well as the fabrication process are discussed in this paper.

2. Experiment

All samples were grown on a 2-in (0001) patterned sapphire substrate (PSS) through a Thomas Swan close-coupled showerhead 31 × 2 metalorganic chemical vapor deposition (MOCVD) system. The PSS periodic convex pattern was formed using an inductively coupled plasma etcher. Pattern diameter, spacing, and height of the PSS were 2.5, 1, and 1.6 µm, respectively. During MOCVD growth, trimethylindium, trimethylgallium, trimethylaluminum, and ammonia were used as the source materials of In, Ga, Al, and N, respectively. Bicyclopentadienyl magnesium and silane were used as the p-type and n-type doping sources. The reactor temperature was raised to 500 °C to grow a 20 nm-thick GaN nucleation layer on the PSS in situ. The reactor temperature was then raised to 1050 °C to grow a 2 µm-thick undoped GaN epitaxial layer followed by the deposition of a 2 µm-thick n-GaN layer. Subsequently, a nine-pair InGaN (2.5 nm)/AlGaN (4.5 nm) UV light-emitting MQW structures, named conventional UV LEDs, was produced via a high–low temperature scheme. The growth temperatures of AlGaN and AlN/GaN barrier layers were kept at 820 °C. The growth pressures for AlGaN/InGaN and AlN/GaN/InGaN MQWs are 300 mbar. We varied the growth temperature of the InGaN well from 800 °C to 770 °C to have the UV LEDs emission wavelength of 375, 385, and 395 nm. After the growth of the light-emitting MQWs structure, an AlGaN electron blocking layer (EBL) was grown on AlGaN/InGaN MQWs and AlN/GaN/InGaN MQWs. The details UV LEDs structure, growth temperatures of MQWs, and source-switching sequences of the AlGaN/InGaN and AlN/GaN/InGaN MQWs are showing in the Fig. 1(a) and 1(b), respectively. Thickness and Al% of the AlGaN barrier were approximately 4.5nm and 15%, respectively. The expected thicknesses of the AlN and GaN for the AlN/GaN barrier are approximately 2.5nm and 2.0nm, respectively. A 0.1µm-thick p-GaN layer was deposited following the EBL layer.

 

Fig. 1 (a) UV LEDs structure of the AlGaN/InGaN and AlN/GaN/InGaN MQWs. (b) The growth temperatures and source-switching sequences of of the AlGaN/InGaN and AlN/GaN/InGaN MQWs.

Download Full Size | PPT Slide | PDF

Subsequently, standard processing steps were performed to fabricate 1143 µm × 1143 µm LED chips with indium tin oxide in the upper contact. The current–voltage (I–V) characteristics of the fabricated LEDs were then measured using an HP-4156C semiconductor parameter analyzer with a 100-mA current limit. At a high current injection, a Keithley 2400 source meter was used to measure the I–V characteristics of these LEDs. The output power and emission wavelength of the LEDs were measured at room temperature using a calibrated integrating sphere and a spectrometer (Ocean Optics USB2000).

3. Results and discussion

Figure 2(a) reveals the I–V characteristics of GaN-based UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs. All UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs showed forward voltages (Vf) in the range of 3.21 V to 3.29 V at 350 mA. The ideality factors of the forward I–V characteristics of UV LEDs with AlGaN/InGaN MQWs in the applied voltage range of 3.23 V to 3.31 V ranged between 1.75 and 1.78. However, UV LEDs with AlN/GaN/InGaN MQWs revealed a smaller ideality factor in the range of 1.62 and 1.73 compared with that of UV LEDs with AlGaN/InGaN MQWs. The improved ideality factor of the UV LED with AlN/GaN/InGaN MQWs indicates less defect-related leakage current recombination. Moreover, Fig. 2(b) shows that the reverse leakage currents at –20 V of UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs ranged between −1900 to −5000 nA and −98 to −385 nA, respectively. The reverse leakage current at −20 V of the UV LED with AlN/GaN/InGaN MQWs was nearly two orders less than that of the UV LED with AlGaN/InGaN MQWs.

 

Fig. 2 (a) Forward I–V and (b) reverse I–V characteristics of GaN-based UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs.

Download Full Size | PPT Slide | PDF

Figure 3(a) shows the light output powers of UV LEDs at 350-mA current injections as a function of emission peak wavelength. The light output powers of 374.74, 385.55, and 393.2 nm of AlGaN/InGaN MQW of UV LEDs were 60.81, 402.32, and 466.65 mW, respectively. In addition, the light output powers at the emission peak wavelength 374.94, 385.98, 392.13 nm of UV LEDs with AlN/GaN/InGaN MQWs were 77.05, 445.96, 478.0 mW, respectively. It is found that the AlN/GaN/InGaN MQWs UV LEDs have larger 350-mA light output power than that of AlGaN/InGaN MQW UV LEDs for the all emission peak wavelength. One of reasons for the improved 350-mA light output power of AlN/GaN/InGaN MQWs UV LEDs can be attributed to the staggered QW structure of AlN/GaN/InGaN MQWs. The staggered QW structure could improve the electron hole overlap in the QWs with internal field [20]. The UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs degraded their 350-mA light output power as the emission peak wavelength shortened, which could be attributed to the increased influence of the dislocation of the n-GaN layers and the weak carrier confinement of the QW. We take a look at the emission peak wavelength dependent average output power enhancement factor showing in inset of Fig. 3(a), which is defined the light output power differences between AlN/GaN/InGaN MQWs UV LEDs and AlGaN/InGaN MQWs UV LEDs at 350 mA divided by the light output power of AlGaN/InGaN MQWs UV LEDs at 350 mA. It is found that the enhancement factor of the 350-mA output power of AlN/GaN/InGaN MQW UV LEDs increased as the emission peak wavelength decreased as shown in the inset in Fig. 3(a). The output power enhancement factor can reach around 26.7% at the emission peak wavelength of 375 nm but reach only around 2.43% at emission peak wavelength of 395 nm. The results show that the light output power of the LEDs with short-peaked UV wavelength is improved by AlN/GaN/InGaN MQWs because of the enhanced carrier confinement.

 

Fig. 3 (a) Output power of UV LEDs at 350-mA current injections and (b) external quantum efficiency (EQE) of UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs. The inset in Fig. 3 (a) shows the emission wavelength dependent the output power enhancement factor.

Download Full Size | PPT Slide | PDF

AlN/GaN/InGaN MQW UV LEDs would also improve light output power at high current injection. Figure 3(b) shows the injection current-dependent external quantum efficiency (EQE) of the 375-, 385-, and 395-nm emission wavelength UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs. AlN/GaN/InGaN MQW UV LEDs with 395-nm emission wavelength shows less EQE than AlGaN/InGaN MQW UV LEDs at an injection current below 200 mA. When the injection current is larger than 200 mA, the EQE of AlN/GaN/InGaN MQW UV LEDs with 395-nm emission wavelength becomes larger than that of AlGaN/InGaN MQW UV LEDs. The AlN/GaN barrier may cause more lattice mismatch in InGaN wells with 395-nm emission wavelength, resulting in the crystal quality degradation of InGaN wells or increase the piezoelectric field in InGaN wells. It would also degrade the EQE of UV LEDs under low current injection. However, for InGaN wells with 395-nm emission wavelength, AlN/GaN barrier would have better carrier confinement than the AlGaN barrier under high current injection. It would cause the 395-nm emission wavelength UV LEDs with AlN/GaN/InGaN MQWs to have larger EQEs than AlGaN/GaN MQWs at an injection current more than 200 mA. However, AlN/GaN/InGaN MQW UV LEDs with 375-nm and 385-nm emission wavelengths have larger EQEs than AlGaN/InGaN MQW UV LEDs with emission wavelengths of 375 nm and 385 nm at all injection current levels. The carrier confinement of the AlGaN barrier would be good for InGaN wells with 395-nm emission wavelength under low current injection. With a reduction in the emission wavelength of UV LEDs, the strain within InGaN wells would be reduced for both AlGaN and AlN/GaN barriers. Therefore, carrier confinement would become the dominant effect of the 375-nm and 385-nm emission wavelength UV LEDs. As AlN/GaN/InGaN MQWs have superior carrier confinement than AlGaN/InGaN MQWs, AlN/GaN/InGaN MQW UV LEDs with 375-nm and 385-nm emission wavelengths have larger EQEs than AlGaN/InGaN MQWs UV LEDs at all injection current levels.

Figure 4 shows the SEM images of AlGaN/InGaN and AlN/GaN/InGaN MQWs. AlGaN/InGaN MQWs have large pits each with a size of around 1.3 μm based on low magnification SEM observation. By contrast, AlN/GaN/InGaN MQWs do not show any large-sized pits on the surface under the same SEM observation condition. However, AlN/GaN/InGaN and AlGaN/InGaN MQWs exhibit small pits each with a size of around 90nm on the surface when we zoomed in on the smooth area of both samples as shown in the insets in Figs. 4(a) and 4(b), respectively. Furthermore, AlN/GaN/InGaN MQWs have a pit density of 1.01 µm−2, which is smaller than AlGaN/InGaN MQWs’ pit density of 2.01 µm−2. To understand the microstructure of AlGaN/InGaN and AlN/GaN/InGaN MQWs we have fulfilled the high resolution transmission electron microscope (HRTEM) (FEI Tecnai F20 TEM) observation on AlGaN/InGaN and AlN/GaN/InGaN MQWs UV LEDs with emission peak wavelength of 385nm. Figure 5 (a) and 5(b) show the TEM images of the AlGaN/InGaN and AlN/GaN/InGaN MQWs UV LEDs, respectively. The thicknesses of the InGaN wells measured from HRTEM images ranging from 2.5 to 3.0 nm meet the designed deposition conditions. It is found that the AlGaN/InGaN MQWs does not show a steep interface between the AlGaN and InGaN layer. And the InGaN wells thickness shows a significant fluctuation in the AlGaN/InGaN MQWs. In contrast, the AlN/GaN/InGaN MQWs shows a clear interface between the AlN/GaN barrier and InGaN wells. And the InGaN wells thickness indicates a better uniformity in the AlN/GaN/InGaN MQWs. Therefore, the enhanced 350mA light output power of the AlN/GaN/InGaN MQWs UV LEDs is considered to result from the better barrier/well interfacial structure and thickness uniformity of AlN/GaN/InGaN MQWs than those of AlGaN/InGaN MQWs. However, we could not reveal the individual AlN layer and GaN layer in our designed AlN/GaN barrier form the HRTEM images. One of reasons for this problem is attributed to the composition fluctuation in each atomic layer deposited by MOCVD. So, composition fluctuation exists in layers of MQW, and results in no defined boundaries between AlN-GaN in HRTEM images. The other reason for this problem might be from that the Al atoms and Ga atoms might inter-remix or inter-diffuse with the in front GaN layer during the AlN growth. Energy dispersive X-ray (EDX) line profiles by scanning transmission electron microscope (STEM) mode from both UV LEDs samples, as shown in Fig. 6, displayed the elemental distribution of the Al, In, and Ga atoms through a distance of 50 nm in both AlGaN/InGaN MQWs and AlN/GaN/InGaN MQWs. These results indicated that the composition iteration in AlN/GaN/InGaN MQWs is more controllable in processes of deposition and annealing due to those Al rich layers. It could also improve the carrier confinement of the UV LEDs by introducing AlN/GaN/InGaN MQWs.

 

Fig. 4 SEM images of the surfaces of (a) AlGaN/InGaN and (b) AlN/GaN/InGaN MQWs. The insets in (a) and (b) are enlarged SEM images of the smooth surface areas of AlGaN/InGaN and AlN/GaN/InGaN MQWs, respectively.

Download Full Size | PPT Slide | PDF

 

Fig. 5 The TEM images of the (a)AlGaN/InGaN MQWs and (b)AlN/GaN/InGaN MQWs.

Download Full Size | PPT Slide | PDF

 

Fig. 6 EDX line profiles by STEM mode from the (a)AlGaN/InGaN MQWs and (b)AlN/GaN/InGaN MQWs UV LEDs samples.

Download Full Size | PPT Slide | PDF

AlN/GaN/InGaN MQWs have better InGaN thickness uniformity, well/barrier interface quality and less large size V-shaped pit density (size more than 1 μm) than AlGaN/InGaN MQWs. These effects might be the reasons behind AlN/GaN/InGaN MQW UV LEDs having less reverse leakage currents at −20V. Also worth noting is that AlN/GaN/InGaN MQW UV LEDs have the 2-kV human body mode (HBM) electrostatic discharge (ESD) pass yield of 85% which is 15% more than the 2-kV HBM ESD pass yield of AlGaN/InGaN MQW UV LEDs of 70%. The improved ESD pass yield should be again attributed to better interface quality and less large size V-shaped pit density than AlGaN/InGaN MQWs.

Figure 7 indicates the light output and reverse leakage of current reliabilities of the emission peak wavelength 385 nm of UV LEDs with AlN/GaN/InGaN MQWs and AlGaN/InGaN MQWs. The UV LEDs were aged at 350 mA of injection current at 80 °C for 196 h. Within 196 h, AlN/GaN/InGaN MQW UV LEDs revealed an output power drop of around 3.6%, which is less than the approximated 8.7% output power drop of AlGaN/InGaN MQW UV LEDs [Fig. 7(b)]. The reverse leakage currents at −5 V of the AlN/GaN/InGaN MQW and AlGaN/InGaN MQW UV LEDs [Fig. 7(a)] increased with the aging time. However, the AlGaN/InGaN MQW UV LEDs demonstrated much larger reverse leakage current increments with the aging time than AlN/GaN/InGaN MQW UV LEDs. Meneghni etal [21]. have reported that generation defects and doping redistribution in the active region would degrade the power output and increase the reverse leakage current of UV LEDs during electrical aging. Reports presented evidence for the diffusion of doping/impurities (e.g., Mg and Si) toward the active region of LEDs [22,23] and suggested that the presence of defects play a significant role in easing the diffusion process even at relatively low temperatures [21]. AlN/GaN/InGaN MQWs have better InGaN thickness uniformity, well/barrier interface quality and less large size V-shaped pit density than AlGaN/InGaN MQWs. Therefore, the improved reliability of AlN/GaN/InGaN MQW UV LEDs can again be attributed to better InGaN thickness uniformity, well/barrier interface quality and less large size V-shaped pit density of AlN/GaN/InGaN MQWs.

 

Fig. 7 (a) Reverse leakage current at −5V and (b) light output power reliability of UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs.

Download Full Size | PPT Slide | PDF

4. Conclusion

In summary, we have demonstrated that AlN/GaN/InGaN MQW UV LEDs can improve light output power. UV LEDs with AlN/GaN/InGaN MQWs have 350-mA forward voltages (Vf) in the range of 3.21 V to 3.29 V, which are similar to those of conventional AlGaN/InGaN MQW UV LEDs. The 350-mA output power at each emission peak wavelength of AlN/GaN/InGaN MQW UV LEDs is greater than that of the corresponding emission peak wavelength of AlGaN/InGaN MQW UV LEDs. The light output power enhancement can reach around 26.7% in magnitude at the emission peak wavelength of 375 nm, but can reach only around 2.43% at emission peak wavelength of 395 nm. Moreover, compared with AlGaN/InGaN MQWs, AlN/GaN/InGaN MQWs present better InGaN thickness uniformity, well/barrier interface quality and less large size pits, thereby having less reverse leakage currents at −20V. AlN/GaN/InGaN MQW UV LEDs also have 2-kV HBM ESD pass yield of 85%, which is larger than AlGaN/InGaN MQW UV LEDs’ 70% 2-kV HBM ESD pass yield. In addition, AlN/GaN/InGaN MQW UV LEDs demonstrate improved reliability characteristic. AlN/GaN/InGaN MQW UV LEDs show a light output power drop of around 3.6%, whereas AlGaN/InGaN MQW UV LEDs exhibit 8.7% light output power drop within 196 h.

Acknowledgments

The authors are grateful to the National Science Council of Taiwan for their financial support under Contract Nos. NSC101-2221-E-006-066-MY3 and 102-3113-P-009-007-CC2. This research was also made possible through the Advanced Optoelectronic Technology Center, National Cheng Kung University, as a project of the Ministry of Education of Taiwan, and through the financial support of the Bureau of Energy, Ministry of Economic Affairs of Taiwan, under Contract No. 102-E0603. We would like to especially thank Dr. J. S. Bow for performing the TEM observation on AlGaN/InGaN and AlN/GaN/InGaN MQWs UV LEDs.

References and links

1. Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006). [CrossRef]  

2. S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995). [CrossRef]  

3. T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002). [CrossRef]  

4. D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002). [CrossRef]  

5. S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997). [CrossRef]  

6. P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001). [CrossRef]  

7. M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

8. A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007). [CrossRef]  

9. M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999). [CrossRef]  

10. M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007). [CrossRef]  

11. J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

12. M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000). [CrossRef]  

13. Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013). [CrossRef]  

14. R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010). [CrossRef]  

15. Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014). [CrossRef]  

16. Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014). [CrossRef]  

17. L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002). [CrossRef]  

18. Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013). [CrossRef]   [PubMed]  

19. K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013). [CrossRef]  

20. H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008). [CrossRef]  

21. M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010). [CrossRef]  

22. S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004). [CrossRef]  

23. S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009). [CrossRef]  

References

  • View by:
  • |
  • |
  • |

  1. Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
    [Crossref]
  2. S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
    [Crossref]
  3. T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
    [Crossref]
  4. D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
    [Crossref]
  5. S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
    [Crossref]
  6. P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001).
    [Crossref]
  7. M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).
  8. A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
    [Crossref]
  9. M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
    [Crossref]
  10. M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
    [Crossref]
  11. J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).
  12. M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
    [Crossref]
  13. Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
    [Crossref]
  14. R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
    [Crossref]
  15. Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
    [Crossref]
  16. Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
    [Crossref]
  17. L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
    [Crossref]
  18. Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
    [Crossref] [PubMed]
  19. K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
    [Crossref]
  20. H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
    [Crossref]
  21. M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
    [Crossref]
  22. S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
    [Crossref]
  23. S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
    [Crossref]

2014 (2)

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

2013 (3)

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

2010 (2)

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

2009 (1)

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

2008 (1)

H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
[Crossref]

2007 (3)

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

2006 (1)

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

2005 (1)

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

2004 (1)

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

2002 (3)

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

2001 (1)

P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001).
[Crossref]

2000 (1)

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

1999 (1)

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

1997 (1)

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

1995 (1)

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

Allerman, A. A.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Anazawa, K.

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Ao, J. P.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Asif Khan, M.

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Azuhata, T.

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

Bai, J.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Beak, S.-H.

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

Bicknell-Tassius, R.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Breiland, W. G.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Bykhovsky, A.

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Chandrasekhar, D.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Chang, S. J.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Chen, C. H.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Chen, J. F.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Chen, R.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Chichibu, S.

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

Craford, M. G.

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

Cross, K. C.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Dai, Q.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Deguchi, K.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Demir, H. V.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

DenBaars, S. P.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Dikme, Y.

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Ee, Y.-K.

H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
[Crossref]

Einfeldt, S.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Erdem, T.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Farrell, R. M.

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Figiel, J. J.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Fischer, A. J.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Fujii, K.

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Fujito, K.

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Fullmer, K. W.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Gaska, R.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Goto, S.

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

Ha, K. H.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Haeger, D. A.

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Hassanet, S.

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Hino, T.

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

Hoffmann, V.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Hsu, P. S.

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Ikeda, M.

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

Izumi, Y.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Ji, Y.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Ju, Z.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Kent, P. R. C.

P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001).
[Crossref]

Khan, M.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Kim, H.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Kim, J. K.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Kim, J.-Y.

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

Kim, K. K.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Kim, M.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Knauer, A.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Kneissl, M.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Kolbe, T.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Koleske, D. D.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Kueller, V.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Kuo, C. H.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Kurtz, S. R.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Kwon, M.-K.

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

Kyaw, Z.

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Lai, W. C.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Lee, S. N.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Lee, Y. B.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Lester, S. D.

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

Li, H. D.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Li, J.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Liu, W.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Liu, Y. H.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Lu, F.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Meneghesso, G.

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

Meneghini, M.

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

Mitchell, C. C.

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

Mukai, T.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Mura, G.

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

Nakamura, S.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

Nakano, Y.

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Nam, O. H.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Narita, J.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Narukawa, Y.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Paek, H. S.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Park, I.-K.

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

Park, S. J.

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

Park, Y.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Piprek, J.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Ponce, F. A.

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

Ronald A Arif, H. Z.

H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
[Crossref]

Sakai, S.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Sakamoto, T.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Schubert, E. F.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Schubert, M. F.

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

Sheu, J. K.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Shi, S. L.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Shur, M. S.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Simin, G.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Smith, D. J.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Son, J. K.

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Sota, T.

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

Speck, J. S.

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Steigerwald, D. A.

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

Su, Y. K.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Sugiyama, M.

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

Sun, H.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Sun, X. W.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Takeya, M.

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

Tamulaitis, G.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Tan, S. T.

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Tansu, N.

H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
[Crossref]

Tazzoli, A.

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

Tomiya, S.

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

van Look, J.-R.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Wang, L.

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Wang, T.

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

Wang, Y. J.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Wen, T. C.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Weyers, M.

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Wu, L. W.

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

Xu, S. J.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Yamada, T.

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Yang, H.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Yang, J. W.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

Zanoni, E.

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

Zhang, X.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Zhang, Z.-H.

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Z.-H. Zhang, S. T. Tan, Y. Ji, W. Liu, Z. Ju, Z. Kyaw, X. W. Sun, and H. V. Demir, “A PN-type quantum barrier for InGaN/GaN light emitting diodes,” Opt. Express 21(13), 15676–15685 (2013).
[Crossref] [PubMed]

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

Zhao, D. G.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Zhao, Y.

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

Zhu, J. J.

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

Zukauskas, A.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Zunger, A.

P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001).
[Crossref]

zur Loye, H.-C.

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

Appl. Phys. Lett. (10)

D. D. Koleske, A. J. Fischer, A. A. Allerman, C. C. Mitchell, K. C. Cross, S. R. Kurtz, J. J. Figiel, K. W. Fullmer, and W. G. Breiland, “Improved brightness of 380 nm GaN light emitting diodes through intentional delay of the nucleation island coalescence,” Appl. Phys. Lett. 81(11), 1940–1942 (2002).
[Crossref]

S. Chichibu, T. Azuhata, T. Sota, and S. Nakamura, “Luminescences from localized states in InGaN epilayers,” Appl. Phys. Lett. 70(21), 2822–2825 (1997).
[Crossref]

P. R. C. Kent and A. Zunger, “Carrier localization and the origin of luminescence in cubic InGaN alloys,” Appl. Phys. Lett. 79(13), 1977–1979 (2001).
[Crossref]

S. D. Lester, F. A. Ponce, M. G. Craford, and D. A. Steigerwald, “High Dislocation Densities in High-Efficiency Gan-Based Light-Emitting-Diodes,” Appl. Phys. Lett. 66(10), 1249–1251 (1995).
[Crossref]

M. Asif Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, and A. Bykhovsky, “Piezoelectric doping in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 75(18), 2806 (1999).
[Crossref]

M. Kim, M. F. Schubert, Q. Dai, J. K. Kim, E. F. Schubert, J. Piprek, and Y. Park, “Origin of efficiency droop in GaN-based light-emitting diodes,” Appl. Phys. Lett. 91(18), 183507 (2007).
[Crossref]

R. M. Farrell, P. S. Hsu, D. A. Haeger, K. Fujito, S. P. DenBaars, J. S. Speck, and S. Nakamura, “Low-threshold-current-density AlGaN-cladding-free m-plane InGaN/GaN laser diodes,” Appl. Phys. Lett. 96(23), 231113 (2010).
[Crossref]

Z.-H. Zhang, W. Liu, Z. Ju, S. T. Tan, Y. Ji, Z. Kyaw, X. Zhang, L. Wang, X. W. Sun, and H. V. Demir, “Self-screening of the quantum confined Stark effect by the polarization induced bulk charges in the quantum barriers,” Appl. Phys. Lett. 104(24), 243501 (2014).
[Crossref]

Y. Ji, W. Liu, T. Erdem, R. Chen, S. T. Tan, Z.-H. Zhang, Z. Ju, X. Zhang, H. Sun, X. W. Sun, Y. Zhao, S. P. DenBaars, S. Nakamura, and H. V. Demir, “Comparative study of field-dependent carrier dynamics and emission kinetics of InGaN/GaN light-emitting diodes grown on (11 2 ̄ 2) semipolar versus (0001) polar planes,” Appl. Phys. Lett. 104(14), 143506 (2014).
[Crossref]

M. Khan, J. W. Yang, G. Simin, R. Gaska, M. S. Shur, H.-C. zur Loye, G. Tamulaitis, A. Zukauskas, D. J. Smith, D. Chandrasekhar, and R. Bicknell-Tassius, “Lattice and energy band engineering in AlInGaN/GaN heterostructures,” Appl. Phys. Lett. 76(9), 1161 (2000).
[Crossref]

IEEE J. Quantum Electron. (2)

L. W. Wu, S. J. Chang, T. C. Wen, Y. K. Su, J. F. Chen, W. C. Lai, C. H. Kuo, C. H. Chen, and J. K. Sheu, “Influence of Si-Doping on the Characteristics of InGaN–GaN Multiple Quantum-Well Blue Light Emitting Diodes,” IEEE J. Quantum Electron. 38(5), 446–450 (2002).
[Crossref]

H. Z. Ronald A Arif, Y.-K. Ee, and N. Tansu, “Spontaneous Emission and Characteristics of Staggered InGaN Quantum-Well Light-Emitting Diodes,” IEEE J. Quantum Electron. 44(6), 573–580 (2008).
[Crossref]

IEEE J. Sel. Top. Quantum Electron. (1)

S. Tomiya, T. Hino, S. Goto, M. Takeya, and M. Ikeda, “Dislocation related issues in the degradation of GaN-based laser diodes,” IEEE J. Sel. Top. Quantum Electron. 10(6), 1277–1286 (2004).
[Crossref]

IEEE Photon. Technol. Lett. (1)

J. Li, S. L. Shi, Y. J. Wang, S. J. Xu, D. G. Zhao, J. J. Zhu, H. Yang, and F. Lu, “Violet electroluminescence of AlInGaN–InGaN Multiquantum-well light-emitting diodes: quantum-confined Stark effect and heating effect,” IEEE Photon. Technol. Lett. 19(10), 789–791 (2007).

IEEE Trans. Electron. Dev. (1)

M. Meneghini, A. Tazzoli, G. Mura, G. Meneghesso, and E. Zanoni, “A Review on the Physical Mechanisms That Limit the Reliability of GaN-Based LEDs,” IEEE Trans. Electron. Dev. 57(1), 108–118 (2010).
[Crossref]

J. Appl. Phys. (1)

M.-K. Kwon, I.-K. Park, S.-H. Beak, J.-Y. Kim, and S. J. Park, “Si delta doping in a GaN barrier layer of InGaN/GaN multi-quantum-well for an efficient ultraviolet light-emitting diode,” J. Appl. Phys. 97(10), 106–109 (2005).

J. Cryst. Growth (2)

T. Wang, Y. H. Liu, Y. B. Lee, Y. Izumi, J. P. Ao, J. Bai, H. D. Li, and S. Sakai, “Fabrication of high performance of AlGaN/GaN-based UV light-emitting diodes,” J. Cryst. Growth 235(1-4), 177–182 (2002).
[Crossref]

K. Anazawa, S. Hassanet, K. Fujii, Y. Nakano, and M. Sugiyama, “Growth of strain-compensated InGaN/AlN multiple quantum wells on GaN by MOVPE,” J. Cryst. Growth 370, 82–86 (2013).
[Crossref]

J. Disp. Technol. (1)

Z.-H. Zhang, S. T. Tan, Z. Ju, W. Liu, Y. Ji, Z. Kyaw, Y. Dikme, X. W. Sun, and H. V. Demir, “On the Effect of Step-Doped Quantum Barriers in InGaN/GaN Light Emitting Diodes,” J. Disp. Technol. 9(4), 226–233 (2013).
[Crossref]

J. Electroceram. (1)

S. N. Lee, H. S. Paek, J. K. Son, H. Kim, K. K. Kim, K. H. Ha, O. H. Nam, and Y. Park, “Effects of Mg dopant on the degradation of InGaN multiple quantum wells in AlInGaN-based light emitting devices,” J. Electroceram. 23(2-4), 406–409 (2009).
[Crossref]

Jpn. J. Appl. Phys. (1)

Y. Narukawa, J. Narita, T. Sakamoto, K. Deguchi, T. Yamada, and T. Mukai, “Ultra-high efficiency white light emitting diodes,” Jpn. J. Appl. Phys. 45(41), L1084–L1086 (2006).
[Crossref]

Opt. Express (1)

Proc. SPIE (1)

A. Knauer, V. Kueller, S. Einfeldt, V. Hoffmann, T. Kolbe, J.-R. van Look, J. Piprek, M. Weyers, and M. Kneissl, “Influence of the barrier composition on the light output of InGaN multiple-quantum-well ultraviolet light emitting diodes,” Proc. SPIE 6797, 67970X (2007).
[Crossref]

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (7)

Fig. 1
Fig. 1 (a) UV LEDs structure of the AlGaN/InGaN and AlN/GaN/InGaN MQWs. (b) The growth temperatures and source-switching sequences of of the AlGaN/InGaN and AlN/GaN/InGaN MQWs.
Fig. 2
Fig. 2 (a) Forward I–V and (b) reverse I–V characteristics of GaN-based UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs.
Fig. 3
Fig. 3 (a) Output power of UV LEDs at 350-mA current injections and (b) external quantum efficiency (EQE) of UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs. The inset in Fig. 3 (a) shows the emission wavelength dependent the output power enhancement factor.
Fig. 4
Fig. 4 SEM images of the surfaces of (a) AlGaN/InGaN and (b) AlN/GaN/InGaN MQWs. The insets in (a) and (b) are enlarged SEM images of the smooth surface areas of AlGaN/InGaN and AlN/GaN/InGaN MQWs, respectively.
Fig. 5
Fig. 5 The TEM images of the (a)AlGaN/InGaN MQWs and (b)AlN/GaN/InGaN MQWs.
Fig. 6
Fig. 6 EDX line profiles by STEM mode from the (a)AlGaN/InGaN MQWs and (b)AlN/GaN/InGaN MQWs UV LEDs samples.
Fig. 7
Fig. 7 (a) Reverse leakage current at −5V and (b) light output power reliability of UV LEDs with AlGaN/InGaN and AlN/GaN/InGaN MQWs.

Metrics