Abstract

The enhanced efficiency of the crystalline silicon (c-Si) solar cell with nanopillar arrays (NPAs) was demonstrated by deployment of CdS quantum dots (QDs). The NPAs was fabricated by the colloidal lithography and reactive-ion etching techniques. Under a simulated one-sun condition, the device with CdS QDs shows a 33% improvement of power conversion efficiency, compared with the one without QDs. For further investigation, the excitation spectrum of photoluminescence (PL), absorbance spectrum, current-voltage (I-V) characteristics, reflectance and external quantum efficiency of the device was measured and analyzed. It is noteworthy that the enhancement of efficiency could be attributed to the photon down-conversion, the antireflection, and the improved electrical property.

©2011 Optical Society of America

1. Introduction

Single crystalline and amorphous silicon solar cells have been important research topics for decades due to their environmental-friendly and stable characteristics, good power conversion efficiency, and mature semiconductor industrial supports. However, there are still many problems in Si-based solar cells needed to be resolved in order to achieve high efficiency. Especially, the high contrast of refractive index of silicon causes a high Fresnel reflectivity at silicon-air interfaces and severely limits the performance of Si-based optoelectronic devices [1, 2]. In order to reduce Fresnel reflection in the solar cells, effective antireflective coatings (ARCs) have been developed [3-5]. The general single layer or multilayer ARC is composed of a quarter wavelength stack of dielectrics with different refractive indices, such as silicon nitride or silicon dioxide [6-7]. However, these complicated dielectric layers need expensive equipment with high-vacuum chamber, and precise layer thickness control. All of these measures could put the overall cost of solar cells unbearable.

Consequently, some research laboratories have developed sub-wavelength structures to eliminate such kind of reflection and improved cell efficiency, such as nanowire or nanotips [8-10], and it is more stable and enduring than surface coatings since only one material is involved. The basic purpose of this technique is to introduce an effective intermediate refractive index layer between air and the substrate material by the spatial profile of nanostructures [11-17]. Ideally, a tapered profile with sharp tips can provide this feature in terms of refractive index gradient. However, such nanostructures are not preferred in solar cell due to considerable surface recombination.

Besides using ARC to pass more lights into the solar cell, we also have to fully utilize the available solar energy as efficient as possible. However, under the ultraviolet (UV) and near-UV illumination, most of photons are absorbed near the surface of the cell and the collection probability of the generated electron-hole pairs near surface of the Si solar cells is very poor, so the short-wavelength part of the solar spectrum cannot be used completely by Si solar cells with ordinary design.

In this work, we investigate a method by combining the c-Si Nano Pillar Arrays (NPAs) solar cell with CdS QDs layers together, which improves the power conversion efficiency by nearly 33%, compared with the c-Si NPA solar cell without CdS QDs layers. The enhancement was confirmed by the photovoltaic I–V characteristics and the quantum efficiency measurement. It is found that with CdS QDs layers solar cell can improve cell efficiency, especially in the short-circuit current and fill-factor. Based on the spectral response and optical measurement, we demonstrate that CdS QDs layers not only have the capability for photon down-conversion in ultraviolet region but also provide extra antireflection capability and current conductivity for the improvement of Si-based solar cell efficiency.

2. Process and structure

In this experiment, we use colloidal lithography method [18-22] to fabricate c-Si NPA solar cell. As the processes are schematically illustrated in Fig. 1(a) , first, a monolayer of self-assembled 600 nm polystyrene (PS) nanospheres with a plurality of 10 wt% was spin-cast onto the surface of a p-type c-Si substrate. A nearly-close-packed 600 nm PS nanospheres monolayer was then obtained on the c-Si substrate through tuning the degree of hydrophilicity, spinning speed, and the mixture concentration. After steady air-drying for 15 minute, the sample shown in Fig. 1(a) was etched by an inductively coupled plasma reactive ion etching (ICP-RIE) system, where a reactive gas Cl2 was introduced to bombard the nanospheres and the underlying c-Si substrate simultaneously with an RF power of 1000 W, a bias power of 150 W, under a 5 mTorr pressure at 60°C for 140 seconds. The sample was brushed and dipped into a pure acetone solution for 5 minutes at room temperature, which resulted in nearly close-packed NPA on the c-Si surface, as shown in Fig. 1(b). Next, the NPA substrate was doped using phosphorus oxychloride (POCl3) as the diffusion source to form an n-type layer, about 200 nm deep from the surface. After the removal of the phosphosilicate glass (PSG) layer from the substrate surface with diluted hydrofluoric (HF) acid, as shown in Fig. 1(c), an 80-nm-thick silicon nitride (SiNx) layer was deposited to passivate the surface by using plasma-enhanced chemical vapor deposition (PECVD). Then the front and back metal contacts were screen-printed and a co-firing in a furnace system at 850°C. Finally, a colloidal CdS QDs with a concentration of 5 mg/mL was spun on the surface of c-Si NPA solar cell, as shown in Fig. 1(d). For comparison, the one without the CdS QDs layers was also fabricated simultaneously as the reference.

 figure: Fig. 1

Fig. 1 The schematic fabrication flow for c-Si nanopillar arrays (NPA) solar cell with CdS quantum dots (QDs) layers: (a) spin-cast of nearly-close-packed polystyrene nanospheres monolayer, (b) resulting NPA after dry etching, (c) diffusion of an N-type layer. (d) SiNx deposition and screen printing of the front and back electrodes, and then spin CdS QDs layers on the cell.

Download Full Size | PPT Slide | PDF

In the Fig. 2 (a) , we show the scanning electron microscopic (SEM) image of c-Si NPA in which the periodic pattern is accurately transferred onto the Si substrate after RIE. The height and shape of NPA can be controlled by varying the etching duration and our process control shaped the height of the NPA to be around 550 nm. In order to inspect experimental result of c-Si NPA solar cell after the addition of CdS QDs layers, the transmission electron microscopy (TEM) samples were also prepared using focus ion beam (FIB) techniques. The TEM image was taken near the edge of metal contact and the thickness of the CdS layer is ~6 nm, as shown in Fig. 2 (b). The element of CdS QDs layers was analyzed by Energy Dispersive Spectrometer (EDS), as also shown in (inserts of under corner) the image. Therefore, we can confirm the existence of Cd and S elements on the cell.

 figure: Fig. 2

Fig. 2 (a) A cross-sectional view of scanning electron microscopic (SEM) image of the c-Si nanopillar arrays. (b) A cross-sectional TEM image of edge of metal contact after the integration CdS QDs layers, the size of CdS QDs layers is about 6 nm. The element of CdS QDs layers was analyzed by Energy Dispersive Spectrometer (EDS) (insets of under corner).

Download Full Size | PPT Slide | PDF

3. Photoluminescence and reflectance

Figure 3(a) shows the diagram of CdS QDs absorption and emission spectra. The photoluminescence spectrum shows a peak at 430 nm, and 550 nm excited by photons with 365 nm or shorter wavelengths. The broad peak is attributed to the trap-states emission of CdS QDs [23]. The absorbance spectrum gradually increases from 375nm towards 330 nm. It is obvious that CdS QDs exhibit photon down-conversion from ultraviolet to visible light (from ~330 to 550 nm). This converted light can provide more photons to be harvested in c-Si NPA solar cell. Figure 3(b) shows reflectance spectra by an integrating sphere at the normal incidence of light. The c-Si NPA with CdS QDs layers exhibited superior antireflective properties for the wavelength range of interest, especially in the range of wavelength from 450 nm to 1100 nm, compared with the cell without CdS QDs layers. It is found that the CdS QDs layers provide a better antireflection layer for light harvest.

 figure: Fig. 3

Fig. 3 (a) UV-Vis absorbance (red) and photoluminescence (blue) spectra of CdS QDs measure in toluene. The PLE spectrum was taken at the maximum of PL intensity (~430 nm). For the PL spectrum, the sample was excited by a light beam with 365 nm. (b) The measured reflectance spectra for cells with c-Si nanopillar arrays (NPA) with and without CdS quantum dots (QDs) layers.

Download Full Size | PPT Slide | PDF

4. Measurement and analysis

The photovoltaic I–V characteristics were measured under air mass 1.5 global illumination and room temperature conditions by a class-A solar simulator with a xenon flash tube of IEC 904–9 standard. Figure 4 shows the photovoltaic I–V characteristics of the c-Si NPA solar cell with and without CdS QDs layers. The device characteristics were summarized in Table 1 . The short-circuit current density (Jsc) of the c-Si NPA solar cell with CdS QDs layers can reach 32.03 mA/cm2, meanwhile the power conversion efficiency is increased from 9.45% to 12.57%, corresponding to a 33% enhancement compared with the reference. It is also noticeable that open-circuit voltage (Voc) shows negligible change. Additionally, the fill-factor (FF) is improved, which is an indicator of better series resistance of the device. To further investigate the reason behind this FF improvement, we measure the resistance between individual metal contacts with and without CdS QDs layers under a UV light irradiation of 355nm wavelength. The change brought by the QD coating is significant: the resistances dropped from 43.4 Ω to 29.3 Ω. This 32% reduction in electrical resistance should be the direct cause of our FF improvement. From the photovoltaic IV measurement, we can see the enhancement of the solar cell with QDs layers.

 figure: Fig. 4

Fig. 4 Color online) Photovoltaic I–V characteristics of the c-Si nanopillar arrays (NPA) solar cell with and without CdS quantum dots (QDs) layers.

Download Full Size | PPT Slide | PDF

Tables Icon

Table 1. Current-Voltage Characteristics of c-Si NPA Solar Cells with and without CdS QDs layers.

However, it is still unclear whether this improvement is from down-conversion photons or from other factors. To understand more thoroughly on the interaction of QDs with photons, we measured the spectral response of the external quantum efficiency (EQE). Figure 5(a) shows the EQE of the c-Si NPA solar cell with and without CdS QDs layers, and Fig. 5(b) shows the EQE enhancement factor of the devices with CdS QDs layers, compared with reference cell. The cell with CdS QDs layers shows an enhanced EQE in the range from 320nm to 1100nm. According to Fig. 3(a), the absorbance spectrum gradually increases from 375nm towards 330 nm, and this agrees with the peak position of enhancement of EQE at 335nm, as shown in Fig. 5(b). The overall shape of EQE enhancement resembles the absorption curves in Fig. 3, and we believe this is a strong indication of QD absorption and down-conversion process. Most of electron–hole pairs generated in this UV regime are located near surface of device, and the surface defects consume most of the photo-generated carriers, which lead to inferior cell efficiency in UV wavelength range. Therefore, the addition of CdS QDs layers on the c-Si NPA solar cell can produce photon down-conversion effect, in which QD-originated photons with visible wavelengths can be absorbed in the depletion region, and the power conversion efficiency is improved. On the other hand, when the incident photons’ wavelength is longer than 425nm, the QDs layer is served more like an AR coating, which can also enhance the light harvesting.

 figure: Fig. 5

Fig. 5 (a) Measurement of External quantum efficiency of the fabricated c-Si nanopillar arrays (NPA) solar cell with and without CdS QDs layers. (b) Peak (at ~335 nm wavelengths) of short-wavelength enhancement of in EQE indicates photon down-conversion.

Download Full Size | PPT Slide | PDF

To characterize the contribution of down-conversion effect in the short-wavelength range, we further calculated the effective current due to the down-conversion of CdS QDs layers on the surface of the c-Si NPA solar cell. These photo-generated carriers can be observed directly from the short-circuit currents of a solar cell. The short-circuit density without and with CdS QDs, Jsc and Jsc,QDs can be calculated as follows:

Jsc=ehc×320nm1100nmλ×EQE(λ)×IAM1.5G(λ)dλ
Jsc,QDs=ehc×(320nm400nm[1A(λ)]×λ×EQE(λ)×IAM1.5G(λ)dλ+320nm400nmA(λ)×λ×EQE(λ)×QY×IAM1.5G(λ)dλ+400nm1100nmλ×EQE(λ)×IAM1.5G(λ)dλ)
Where e is the electric charge, h is Plank’s constant, c is the speed of light, λ is the wavelength, A(λ) is the absorption of ultraviolet light of the quantum dots, QY is the average quantum yield of the dots, and IAM1.5G(λ) is the intensity of the AM1.5G solar spectrum. From the Fig. 5(b), the quantum yield (QY) of CdS QDs and wavelength dependent absorption A(λ) of CdS QDs can be estimated by the best fit. The average QY is about 60% and average A(λ) is about 8%. Thus by using the equations above, we can calculate the approximate percentage of enhancement attributed to the down-conversion photons. The ratio of difference in short-circuit currents between different wavelength ranges (UV: down-conversion; Visible & IR: anti-reflection) tells us that the portion of down-conversion photon only make up to 0.5% of the Jsc enhancement. Since we only have very thin QD layers coated on surface and under the single pass condition, we believe the low percentage outcome is conceivable. With this humble start, we could further design an optical structure to improve the absorption of CdS QDs in the future.

So far, we have identified at least two factors which play significant roles in our enhanced solar cell performance: the series resistance improvement and the down-conversion plus anti-reflection effect. The first one is possibly circumstantial since some other results showed impaired electrical conduction after QDs layers deployment [24]. However, in our case, the spread of QD helped the electrical conduction and thus improve the overall fill factor. This part can make up for about 90% of the enhancement in efficiency. The other important factor is from quantum dot itself: the down-conversion in the short-wavelength excitation and the anti-reflection in the longer wavelength range. This part is verified in our case through the EQE measurement. Although it only takes 10% of the enhancement, the potential of using quantum dot as a down-conversion layer in solar cell should not be ignored.

5. Conclusion

In summary, the enhanced efficiency of the crystalline silicon (c-Si) solar cell with nanopillar arrays (NPAs) via CdS QDs layers is demonstrated. It is noticeable that power conversion efficiency can be enhanced effectively by surface spin-cast of CdS QDs. The main mechanism of enhancement includes photon down-conversion, antireflection, and current conductivity. As a result, the overall power conversion efficiency is enhanced by 33%, compared with the c-Si NPA solar cell without CdS QDs layers. Finally, we believe that the CdS QDs layer is suitable for Si-based solar cells, and other related applications in the future.

Acknowledgements

This work is founded by National Science Council in Taiwan under grant number NSC 99-2120-M- 006-002 and NSC-99-2120-M-009-007.

References and links

1. C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett. 5(12), 2438–2442 (2005). [CrossRef]   [PubMed]  

2. Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett. 8(5), 1501–1505 (2008). [CrossRef]   [PubMed]  

3. D. J. Aiken, “High performance anti-reflection coatings for broadband multi-junction solar cells,” Sol. Energy Mater. Sol. Cells 64(4), 393–404 (2000). [CrossRef]  

4. W. H. Southwell, “Gradient-index antireflection coatings,” Opt. Lett. 8(11), 584–586 (1983). [CrossRef]   [PubMed]  

5. D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells 52(1-2), 79–93 (1998). [CrossRef]  

6. J. A. Dobrowolski, D. Poitras, P. Ma, H. Vakil, and M. Acree, “Toward perfect antireflection coatings: numerical investigation,” Appl. Opt. 41(16), 3075–3083 (2002). [CrossRef]   [PubMed]  

7. D. Poitras, J. A. Dobrowolski, T. Cassidy, P. Ma, M. Acree, and H. Vakil, “Toward perfect antireflection coatings. 2. Theory,” Appl. Opt. 43(6), 1286–1295 (2004). [CrossRef]   [PubMed]  

8. K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett. 9(11), 3704–3709 (2009). [CrossRef]   [PubMed]  

9. T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology 19(29), 295203 (2008). [CrossRef]   [PubMed]  

10. J. Y. Jung, Z. Guo, S. W. Jee, H. D. Um, K. T. Park, and J. H. Lee, “A strong antireflective solar cell prepared by tapering silicon nanowires,” Opt. Express 18(S3Suppl 3), A286–A292 (2010). [CrossRef]   [PubMed]  

11. C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett. 93(13), 133109 (2008). [CrossRef]  

12. J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett. 95(3), 033102 (2009). [CrossRef]  

13. Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett. 78(2), 142–143 (2001). [CrossRef]  

14. Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol. 2(12), 770–774 (2007). [CrossRef]   [PubMed]  

15. C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett. 94(5), 051114 (2009). [CrossRef]  

16. G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett. 90(18), 181923 (2007). [CrossRef]  

17. M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express 19(S1Suppl 1), A28–A34 (2011). [CrossRef]   [PubMed]  

18. M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett. 22(1), 12–14 (2010). [CrossRef]  

19. X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J. 3(3), 489–499 (2011). [CrossRef]  

20. Y. K. Ee, P. Kumnorkaew, H. Tong, R. A. Arif, J. F. Gilchrist, and N. Tansu, “Enhancement of Light Extraction Efficiency of InGa Quantum Wells Light-Emitting Diodes with Polydimethylsiloxane Concave Microstructures,” Light-Emitting Diodes: Materials, Devices, and Applications for Solid State Lighting Xiii 7231 (2009).

21. Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron. 15(4), 1218–1225 (2009). [CrossRef]  

22. Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett. 91(22), 221107 (2007). [CrossRef]  

23. Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc. 126(22), 6874–6875 (2004). [CrossRef]   [PubMed]  

24. C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano 4(10), 5849–5854 (2010). [CrossRef]   [PubMed]  

References

  • View by:
  • |
  • |
  • |

  1. C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
    [Crossref] [PubMed]
  2. Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
    [Crossref] [PubMed]
  3. D. J. Aiken, “High performance anti-reflection coatings for broadband multi-junction solar cells,” Sol. Energy Mater. Sol. Cells64(4), 393–404 (2000).
    [Crossref]
  4. W. H. Southwell, “Gradient-index antireflection coatings,” Opt. Lett.8(11), 584–586 (1983).
    [Crossref] [PubMed]
  5. D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
    [Crossref]
  6. J. A. Dobrowolski, D. Poitras, P. Ma, H. Vakil, and M. Acree, “Toward perfect antireflection coatings: numerical investigation,” Appl. Opt.41(16), 3075–3083 (2002).
    [Crossref] [PubMed]
  7. D. Poitras, J. A. Dobrowolski, T. Cassidy, P. Ma, M. Acree, and H. Vakil, “Toward perfect antireflection coatings. 2. Theory,” Appl. Opt.43(6), 1286–1295 (2004).
    [Crossref] [PubMed]
  8. K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
    [Crossref] [PubMed]
  9. T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
    [Crossref] [PubMed]
  10. J. Y. Jung, Z. Guo, S. W. Jee, H. D. Um, K. T. Park, and J. H. Lee, “A strong antireflective solar cell prepared by tapering silicon nanowires,” Opt. Express18(S3Suppl 3), A286–A292 (2010).
    [Crossref] [PubMed]
  11. C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
    [Crossref]
  12. J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
    [Crossref]
  13. Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
    [Crossref]
  14. Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
    [Crossref] [PubMed]
  15. C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
    [Crossref]
  16. G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
    [Crossref]
  17. M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express19(S1Suppl 1), A28–A34 (2011).
    [Crossref] [PubMed]
  18. M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
    [Crossref]
  19. X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
    [Crossref]
  20. Y. K. Ee, P. Kumnorkaew, H. Tong, R. A. Arif, J. F. Gilchrist, and N. Tansu, “Enhancement of Light Extraction Efficiency of InGa Quantum Wells Light-Emitting Diodes with Polydimethylsiloxane Concave Microstructures,” Light-Emitting Diodes: Materials, Devices, and Applications for Solid State Lighting Xiii 7231 (2009).
  21. Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
    [Crossref]
  22. Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
    [Crossref]
  23. Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
    [Crossref] [PubMed]
  24. C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
    [Crossref] [PubMed]

2011 (2)

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express19(S1Suppl 1), A28–A34 (2011).
[Crossref] [PubMed]

2010 (3)

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

J. Y. Jung, Z. Guo, S. W. Jee, H. D. Um, K. T. Park, and J. H. Lee, “A strong antireflective solar cell prepared by tapering silicon nanowires,” Opt. Express18(S3Suppl 3), A286–A292 (2010).
[Crossref] [PubMed]

2009 (4)

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
[Crossref]

2008 (3)

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

2007 (3)

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

2005 (1)

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

2004 (2)

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

D. Poitras, J. A. Dobrowolski, T. Cassidy, P. Ma, M. Acree, and H. Vakil, “Toward perfect antireflection coatings. 2. Theory,” Appl. Opt.43(6), 1286–1295 (2004).
[Crossref] [PubMed]

2002 (1)

2001 (1)

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

2000 (1)

D. J. Aiken, “High performance anti-reflection coatings for broadband multi-junction solar cells,” Sol. Energy Mater. Sol. Cells64(4), 393–404 (2000).
[Crossref]

1998 (1)

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

1983 (1)

Acree, M.

Aiken, D. J.

D. J. Aiken, “High performance anti-reflection coatings for broadband multi-junction solar cells,” Sol. Energy Mater. Sol. Cells64(4), 393–404 (2000).
[Crossref]

Andrä, G.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Arif, R. A.

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Bae, S. Y.

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

Bouhafs, D.

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

Cassidy, T.

Chang, C.

C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
[Crossref]

Chang, Y. C.

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Chang, Y. H.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Chattopadhyay, S.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Chen, C. C.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Chen, H. C.

Chen, K. H.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Chen, L. C.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Chen, Y. F.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Chen, Y. T.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Chikouche, A.

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

Chiu, C. H.

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

Christiansen, S.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Connor, S. T.

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

Cui, Y.

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

Dobrowolski, J. A.

Ee, Y. K.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Falk, F.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Gilchrist, J. F.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Guo, Z.

Hadjipanayis, G. C.

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

Hane, K.

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

Hsu, C. H.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Hsu, C. M.

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

Hsu, J. W. P.

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Hsu, Y. K.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Huang, C. Y.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Huang, Y. F.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Jee, S. W.

Jen, Y. J.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Jiang, Y. T.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Jung, J. Y.

Kanamori, Y.

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

Kumnorkaew, P.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Kuo, H. C.

M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express19(S1Suppl 1), A28–A34 (2011).
[Crossref] [PubMed]

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Kwong, D. L.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Lee, C.

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

Lee, C. S.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Lee, J. H.

Lee, S. T.

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

Lee, Y. J.

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Li, J.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Li, X. H.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Lin, G. R.

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Lin, H. S.

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Lin, S. H.

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

Liu, E. S.

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Liu, T. A.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Lo, H. C.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Lo, P. G. Q.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Lu, T. C.

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

Ma, P.

Manohara, H.

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

McKenzie, B. B.

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Mobasser, S.

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

Moussi, A.

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

Ose, E.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Pan, C. L.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Park, K. T.

Peng, C. Y.

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Peng, K. Q.

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

Peters, D. W.

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Pietsch, M.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Poitras, D.

Ruby, D. S.

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Ruiz, J.

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

Sai, H.

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

Song, R. B.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Southwell, W. H.

Stelzner, T.

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Sun, X.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Tang, M. X.

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

Tansu, N.

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

Tong, H.

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Tsai, M. A.

M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express19(S1Suppl 1), A28–A34 (2011).
[Crossref] [PubMed]

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

Tseng, P. C.

Um, H. D.

Vakil, H.

Wang, C. H.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Wang, D. Y.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Wang, X.

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

Wang, Y. T.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Wong, S. M.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Wu, X. L.

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

Xiao, J. Q.

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

Yang, C.

C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
[Crossref]

Yang, Y. J.

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Yu, H. Y.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Yu, P.

M. A. Tsai, P. C. Tseng, H. C. Chen, H. C. Kuo, and P. Yu, “Enhanced conversion efficiency of a crystalline silicon solar cell with frustum nanorod arrays,” Opt. Express19(S1Suppl 1), A28–A34 (2011).
[Crossref] [PubMed]

C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
[Crossref]

Yu, P. C.

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

Yugami, H.

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

Zhang, G.

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Zhang, Y.

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

Zhao, H. P.

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

Zhao, Y.

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

Zhu, H.

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

ACS Nano (1)

C. Y. Huang, D. Y. Wang, C. H. Wang, Y. T. Chen, Y. T. Wang, Y. T. Jiang, Y. J. Yang, C. C. Chen, and Y. F. Chen, “Efficient Light Harvesting by Photon Downconversion and Light Trapping in Hybrid ZnS Nanoparticles/Si Nanotips Solar Cells,” ACS Nano4(10), 5849–5854 (2010).
[Crossref] [PubMed]

Appl. Opt. (2)

Appl. Phys. Lett. (6)

C. M. Hsu, S. T. Connor, M. X. Tang, and Y. Cui, “Wafer-scale silicon nanopillars and nanocones by Langmuir-Blodgett assembly and etching,” Appl. Phys. Lett.93(13), 133109 (2008).
[Crossref]

J. Li, H. Y. Yu, S. M. Wong, G. Zhang, X. Sun, P. G. Q. Lo, and D. L. Kwong, “Si nanopillar array optimization on Si thin films for solar energy harvesting,” Appl. Phys. Lett.95(3), 033102 (2009).
[Crossref]

Y. Kanamori, K. Hane, H. Sai, and H. Yugami, “100 nm period silicon antireflection structures fabricated using a porous alumina membrane mask,” Appl. Phys. Lett.78(2), 142–143 (2001).
[Crossref]

C. Chang, P. Yu, and C. Yang, “Broadband and omnidirectional antireflection from conductive indium-tin-oxide nanocolumns prepared by glancing-angle deposition with nitrogen,” Appl. Phys. Lett.94(5), 051114 (2009).
[Crossref]

G. R. Lin, Y. C. Chang, E. S. Liu, H. C. Kuo, and H. S. Lin, “Low refractive index Si nanopillars on Si substrate,” Appl. Phys. Lett.90(18), 181923 (2007).
[Crossref]

Y. K. Ee, R. A. Arif, N. Tansu, P. Kumnorkaew, and J. F. Gilchrist, “Enhancement of light extraction efficiency of InGaN quantum wells light emitting diodes using SiO2/polystyrene microlens arrays,” Appl. Phys. Lett.91(22), 221107 (2007).
[Crossref]

IEEE J. Sel. Top. Quantum Electron. (1)

Y. K. Ee, P. Kumnorkaew, R. A. Arif, H. Tong, H. P. Zhao, J. F. Gilchrist, and N. Tansu, “Optimization of Light Extraction Efficiency of III-Nitride LEDs With Self-Assembled Colloidal-Based Microlenses,” IEEE J. Sel. Top. Quantum Electron.15(4), 1218–1225 (2009).
[Crossref]

IEEE Photon. J. (1)

X. H. Li, R. B. Song, Y. K. Ee, P. Kumnorkaew, J. F. Gilchrist, and N. Tansu, “Light Extraction Efficiency and Radiation Patterns of III-Nitride Light-Emitting Diodes With Colloidal Microlens Arrays With Various Aspect Ratios,” IEEE Photon. J.3(3), 489–499 (2011).
[Crossref]

IEEE Photon. Technol. Lett. (1)

M. A. Tsai, P. C. Yu, C. H. Chiu, H. C. Kuo, T. C. Lu, and S. H. Lin, “Self-Assembled Two-Dimensional Surface Structures for Beam Shaping of GaN-Based Vertical-Injection Light-Emitting Diodes,” IEEE Photon. Technol. Lett.22(1), 12–14 (2010).
[Crossref]

J. Am. Chem. Soc. (1)

Y. Zhao, Y. Zhang, H. Zhu, G. C. Hadjipanayis, and J. Q. Xiao, “Low-temperature synthesis of hexagonal (Wurtzite) ZnS nanocrystals,” J. Am. Chem. Soc.126(22), 6874–6875 (2004).
[Crossref] [PubMed]

Nano Lett. (3)

K. Q. Peng, X. Wang, X. L. Wu, and S. T. Lee, “Platinum nanoparticle decorated silicon nanowires for efficient solar energy conversion,” Nano Lett.9(11), 3704–3709 (2009).
[Crossref] [PubMed]

C. Lee, S. Y. Bae, S. Mobasser, and H. Manohara, “A novel silicon nanotips antireflection surface for the micro Sun sensor,” Nano Lett.5(12), 2438–2442 (2005).
[Crossref] [PubMed]

Y. J. Lee, D. S. Ruby, D. W. Peters, B. B. McKenzie, and J. W. P. Hsu, “ZnO nanostructures as efficient antireflection layers in solar cells,” Nano Lett.8(5), 1501–1505 (2008).
[Crossref] [PubMed]

Nanotechnology (1)

T. Stelzner, M. Pietsch, G. Andrä, F. Falk, E. Ose, and S. Christiansen, “Silicon nanowire-based solar cells,” Nanotechnology19(29), 295203 (2008).
[Crossref] [PubMed]

Nat. Nanotechnol. (1)

Y. F. Huang, S. Chattopadhyay, Y. J. Jen, C. Y. Peng, T. A. Liu, Y. K. Hsu, C. L. Pan, H. C. Lo, C. H. Hsu, Y. H. Chang, C. S. Lee, K. H. Chen, and L. C. Chen, “Improved broadband and quasi-omnidirectional anti-reflection properties with biomimetic silicon nanostructures,” Nat. Nanotechnol.2(12), 770–774 (2007).
[Crossref] [PubMed]

Opt. Express (2)

Opt. Lett. (1)

Sol. Energy Mater. Sol. Cells (2)

D. Bouhafs, A. Moussi, A. Chikouche, and J. Ruiz, “Design and simulation of antireflection coating systems for optoelectronic devices: Application to silicon solar cells,” Sol. Energy Mater. Sol. Cells52(1-2), 79–93 (1998).
[Crossref]

D. J. Aiken, “High performance anti-reflection coatings for broadband multi-junction solar cells,” Sol. Energy Mater. Sol. Cells64(4), 393–404 (2000).
[Crossref]

Other (1)

Y. K. Ee, P. Kumnorkaew, H. Tong, R. A. Arif, J. F. Gilchrist, and N. Tansu, “Enhancement of Light Extraction Efficiency of InGa Quantum Wells Light-Emitting Diodes with Polydimethylsiloxane Concave Microstructures,” Light-Emitting Diodes: Materials, Devices, and Applications for Solid State Lighting Xiii 7231 (2009).

Cited By

OSA participates in Crossref's Cited-By Linking service. Citing articles from OSA journals and other participating publishers are listed here.

Alert me when this article is cited.


Figures (5)

Fig. 1
Fig. 1 The schematic fabrication flow for c-Si nanopillar arrays (NPA) solar cell with CdS quantum dots (QDs) layers: (a) spin-cast of nearly-close-packed polystyrene nanospheres monolayer, (b) resulting NPA after dry etching, (c) diffusion of an N-type layer. (d) SiNx deposition and screen printing of the front and back electrodes, and then spin CdS QDs layers on the cell.
Fig. 2
Fig. 2 (a) A cross-sectional view of scanning electron microscopic (SEM) image of the c-Si nanopillar arrays. (b) A cross-sectional TEM image of edge of metal contact after the integration CdS QDs layers, the size of CdS QDs layers is about 6 nm. The element of CdS QDs layers was analyzed by Energy Dispersive Spectrometer (EDS) (insets of under corner).
Fig. 3
Fig. 3 (a) UV-Vis absorbance (red) and photoluminescence (blue) spectra of CdS QDs measure in toluene. The PLE spectrum was taken at the maximum of PL intensity (~430 nm). For the PL spectrum, the sample was excited by a light beam with 365 nm. (b) The measured reflectance spectra for cells with c-Si nanopillar arrays (NPA) with and without CdS quantum dots (QDs) layers.
Fig. 4
Fig. 4 Color online) Photovoltaic I–V characteristics of the c-Si nanopillar arrays (NPA) solar cell with and without CdS quantum dots (QDs) layers.
Fig. 5
Fig. 5 (a) Measurement of External quantum efficiency of the fabricated c-Si nanopillar arrays (NPA) solar cell with and without CdS QDs layers. (b) Peak (at ~335 nm wavelengths) of short-wavelength enhancement of in EQE indicates photon down-conversion.

Tables (1)

Tables Icon

Table 1 Current-Voltage Characteristics of c-Si NPA Solar Cells with and without CdS QDs layers.

Equations (2)

Equations on this page are rendered with MathJax. Learn more.

J s c = e h c × 320 n m 1100 n m λ × E Q E ( λ ) × I A M 1.5 G ( λ ) d λ
J s c , Q D s = e h c × ( 320 n m 400 n m [ 1 A ( λ ) ] × λ × E Q E ( λ ) × I A M 1.5 G ( λ ) d λ + 320 n m 400 n m A ( λ ) × λ × E Q E ( λ ) × Q Y × I A M 1.5 G ( λ ) d λ + 400 n m 1100 n m λ × E Q E ( λ ) × I A M 1.5 G ( λ ) d λ )