Abstract

In this paper, we demonstrate a single-polarization feature out of passive very-large-mode-area fully aperiodic large-pitch fibers. It has been previously shown theoretically that one of the two polarizations of the fundamental mode is selectively coupled to a cladding mode. This coupling does not require fiber bending, which permits us to avoid any decrease in mode effective area. The coupling is achieved owing to boron-doped silica inclusions implemented into the microstructured cladding and acting as stress-applying parts. This mechanism has been assessed experimentally in this work using fibers of two different core diameters: 60 μm and 140 μm, providing mode field areas of $3637{\mathrm{\mu m}}^2$ and $14,590{\mathrm{\mu m}}^2$, respectively, at 1942 nm. The tested fibers have a length of 45 cm and an outer diameter exceeding 1 mm, yielding rod-type fibers. Each sample has been characterized using an unpolarized laser source emitting at 1942 nm. This laser, based on a thulium-doped large-mode-area step-index fiber, has a spectral bandwidth of about 0.5 nm. After passing through a piece of the passive fiber, a polarization extinction ratio higher than 16 dB has been achieved.

© 2017 Optical Society of America

Polarization-maintaining Yb-doped large-mode-area fully aperiodic large-pitch fibers

Rémi du Jeu, Romain Dauliat, Baptiste Leconte, Marie-Alicia Malleville, Raphaël Jamier, Jörg Bierlich, Anka Schwuchow, Kay Schuster, and Philippe Roy
Appl. Opt. 57(29) 8582-8585 (2018)

Broadband single-mode single-polarization passive fully aperiodic large-pitch fibers

Rémi du Jeu, Romain Dauliat, Dia Darwich, Aurélien Benoit, Raphaël Jamier, Kay Schuster, and Philippe Roy
Opt. Lett. 42(9) 1672-1675 (2017)

Demonstration of a homogeneous Yb-doped core fully aperiodic large-pitch fiber laser

Romain Dauliat, Aurélien Benoît, Dia Darwich, Raphaël Jamier, Jens Kobelke, Stephan Grimm, Kay Schuster, and Philippe Roy
Appl. Opt. 55(23) 6229-6235 (2016)

Precompensation of the thermal-induced refractive index changes into a fully aperiodic LPF for heat load resilience

Dia Darwich, Romain Dauliat, Raphaël Jamier, Aurélien Benoit, Kay Schuster, and Philippe Roy
Appl. Opt. 55(29) 8213-8220 (2016)

Single-polarization ultra-large-mode-area Yb-doped photonic crystal fiber

O. Schmidt, J. Rothhardt, T. Eidam, F. Röser, J. Limpert, A. Tünnermann, K.P. Hansen, C. Jakobsen, and J. Broeng
Opt. Express 16(6) 3918-3923 (2008)