Abstract

Motivation for this work includes observations at Lawrence Livermore National Laboratory of a correlation between laser damage thresholds and both the absorption and the nodular-defect density of coatings. Activated oxygen is used to increase the metal-oxidation kinetics at the coated surface during electron-beam deposition. A series of hafnia layers are made with various conditions: two μ-wave configuations, two sources (hafnium and hafnia), and two reactive oxygen pressures. Laser damage thresholds (1064-nm, 10-ns pulses), absorption (at 511 nm), and nodular-defect densities from these coatings are reported. The damage thresholds are observed to increase as the absorption of the coatings decreases. However, no significant increase in damage thresholds are observed with the coatings made from a low nodular-defect density source material (hafnium). Hafnia coatings can be made from hafnium sources that have lower nodular-defect densities, lower absorption, and damage thresholds that are comparable with coatings made from a conventional hafnia source.

© 1993 Optical Society of America

Silicon dioxide and hafnium dioxide evaporation characteristics from a high-frequency sweep e-beam system

Robert Chow and Nick Tsujimoto
Appl. Opt. 35(25) 5095-5101 (1996)

Comparative study of titanium dioxide thin films produced by electron-beam evaporation and by reactive low-voltage ion plating

K. Balasubramanian, X. F. Han, and K. H. Guenther
Appl. Opt. 32(28) 5594-5600 (1993)

Optical coatings deposited by reactive ion plating

Allan J. Waldorf, J. A. Dobrowolski, Brian T. Sullivan, and L. M. Plante
Appl. Opt. 32(28) 5583-5593 (1993)

Laser damage resistance of hafnia thin films deposited by electron beam deposition, reactive low voltage ion plating, and dual ion beam sputtering

Laurent Gallais, Jérémie Capoulade, Jean-Yves Natoli, Mireille Commandré, Michel Cathelinaud, Cian Koc, and Michel Lequime
Appl. Opt. 47(13) C107-C113 (2008)

Damage threshold prediction of hafnia–silica multilayer coatings by nondestructive evaluation of fluence-limiting defects

Zhouling Wu, Christopher J. Stolz, Shannon C. Weakley, James D. Hughes, and Qiang Zhao
Appl. Opt. 40(12) 1897-1906 (2001)