Table I
Uniformity of an ion Assisted Deposited Single Layer of TiO2; Measurements from Spectrophotometry and Photothermal Deflection Spectroscopy
for λ = 633 nm | | | | | | | | |
n | k | tnm | n | k | tnm | n | k | tnm |
2,363 | 2×10−5 | 397 | 2,353 | 2×10−5 | 403 | 2,361 | 2×10−5 | 397 |
position 1 | position 2 | position 3 |
Table II
Measured and Calculated Synchronous Angles of a Fabry-Perot Filter (Glass/HL HL 2H LH LH where H and L are Quarterwave Layers, Respectively, of TiO2 and SiO2 for λ0 = 633 nm)
modes | 0 | 1 | 2 | 3 |
θmeas. | 1°.13 | −16.03 | −19.17 | −35.82 |
θcalc. | −0.05 | −15.70 | −19.8 | −36.3 |
Table III
Distribution of Refractive Indices and Thickness of a Single Layer Deposited on a Large Plane Glass (Characterization by Guided Waves)
d(mm) | 75 | 60 | 45 | 30 | 15 | 0 | 15 | 30 | 45 | 60 | 75 |
n1 | 2,371 | 2,373 | 2,383 | 2,384 | 2,371 | 2,370 | 2,376 | 2,378 | 2,376 | 2,374 | 2,366 |
n2 | 2,367 | 2,369 | 2,373 | 2,375 | 2,371 | 2,372 | 2,372 | 2,371 | 2,371 | 2,369 | 2,367 |
n3 | 2,370 | 2,373 | 2,375 | 2,376 | 2,378 | 2,381 | 2,377 | 2,374 | 2,374 | 2,372 | 2,371 |
t | 401,8 | 401,3 | 400,4 | 400,0 | 399,5 | 399,2 | 399,7 | 399,8 | 400,5 | 401,0 | 401,9 |
↑ center |
Table IV
Measured and Calculated Synchronous Angles of a Double Halfwave Fabry-Perot Filter (Position 2, See Fig. 7): Glass HL HL 2H LH LH L HL HL 2H LH LH where H and L are Quarterwave Layers, Respectively, of TiO2 and SiO2 for λ0 = 590 nm)
| Position 2 (center) | | | | |
meas. | −38.45 | −25.05 | −20.77 | −17.53 | −12.52 | | −0.27 | |
calc. C1 | −38.18 | −25.03 | −20.33 | −17.58 | −13.03 | −0.7 | | −0.6 |
calculation | nH | nL | λc |
C1 | 2.35 | 1.49 | 590 |
| spacer layer | | |
| 2.37 | | |
Table V
Measured and Calculated Synchronous Angles of a Double Halfwave Fabry-Perot Filter (Position 1, See Fig. 7): Glass HL HL 2H LH LH L HL HL 2H LH LH where H and L are Quarterwave Layers, Respectively, of TiO2 and SiO2 for λ0 = 593 nm)
| Position 1 (edge) | | | | |
meas. | −37.8 | −24.93 | −20.93 | −17.93 | −12.85 | | −0.25 | |
calc. C2 | −37.83 | −24.78 | −20.18 | −17.48 | −12.93 | −0.30 | | −0.21 |
calculation | nH | nL | λc |
C2 | 2.35 | 1.49 | 593 |
| spacer layer | | |
| 2.375 | | |