Table I
Percent Change in External Quantum Efficiency at 676.4 nm of DR11 Relative to Central Datum Point; 1-mm Horizontal and Vertical Grid Spacing
−13.98 | −0.23 | 0.04 | 0.05 | 0.07 | 0.04 | 0.04 | −0.74 | −50.55 |
−0.29 | −0.06 | 0.01 | 0.02 | 0.04 | 0.07 | 0.01 | 0.04 | −1.89 |
−0.14 | −0.05 | −0.02 | −0.00 | 0.04 | 0.05 | 0.07 | 0.06 | 0.02 |
−0.20 | −0.11 | 0.04 | −0.02 | 0.00 | 0.03 | 0.03 | 0.03 | −0.03 |
−0.28 | −0.17 | −0.10 | −0.07 | −0.00 | 0.05 | 0.01 | 0.00 | 0.02 |
−0.30 | −0.24 | −0.15 | −0.13 | −0.07 | −0.01 | −0.14 | −0.00 | −0.02 |
−0.38 | −0.32 | −0.23 | −0.12 | −0.34 | −0.06 | −0.04 | −0.09 | −0.13 |
−0.63 | −0.34 | −0.26 | −0.21 | −0.14 | −0.09 | −0.03 | −0.09 | −8.43 |
−31.22 | −1.14 | −0.36 | −0.28 | −0.22 | −0.17 | −0.33 | −7.03 | −64.01 |
Table II
Percent Standard Deviation of the External Quantum Efficiency (Three Measurements at Each Position, 676.4-nm Data); 1-mm Grid Spacing
0.04 | 0.11 | 0.07 | 0.06 | 0.08 | 0.05 | 0.03 | 0.07 | 0.11 |
0.03 | 0.07 | 0.03 | 0.04 | 0.08 | 0.06 | 0.05 | 0.04 | 0.03 |
0.03 | 0.02 | 0.05 | 0.02 | 0.03 | 0.02 | 0.01 | 0.03 | 0.04 |
0.01 | 0.00 | 0.00 | 0.03 | 0.00 | 0.04 | 0.01 | 0.02 | 0.02 |
0.04 | 0.01 | 0.01 | 0.03 | 0.02 | 0.03 | 0.02 | 0.01 | 0.03 |
0.03 | 0.04 | 0.03 | 0.01 | 0.00 | 0.03 | 0.04 | 0.02 | 0.01 |
0.02 | 0.03 | 0.02 | 0.03 | 0.02 | 0.05 | 0.00 | 0.01 | 0.03 |
0.00 | 0.00 | 0.02 | 0.00 | 0.03 | 0.02 | 0.05 | 0.01 | 0.05 |
0.04 | 0.00 | 0.04 | 0.02 | 0.02 | 0.02 | 0.01 | 0.04 | 0.03 |
Table III
Percent Change in Reflectance at 676.4 nm of DR11 Relative to Central Datum Point; 1-mm Grid Spacing
117.03 | 2.18 | −1.38 | −1.37 | −1.39 | −1.58 | −1.31 | 4.57 | 144.98 |
2.51 | −0.22 | −0.46 | −0.75 | −0.67 | −0.68 | −1.18 | −0.89 | 13.56 |
0.61 | 0.43 | −0.08 | −0.14 | −0.28 | −0.35 | −0.47 | −0.43 | −0.19 |
1.27 | 0.84 | 0.55 | 0.13 | −0.08 | −0.10 | −0.13 | −0.22 | 0.37 |
1.58 | 1.16 | 1.00 | 0.59 | −0.00 | −0.12 | 0.07 | −0.13 | 0.09 |
2.01 | 1.32 | 1.36 | 0.99 | 0.36 | 0.22 | −0.01 | 0.20 | 0.39 |
2.50 | 1.78 | 1.70 | 1.06 | 0.18 | 0.44 | 0.38 | 0.54 | 1.03 |
3.88 | 2.28 | 1.86 | 1.36 | 0.69 | 0.94 | 0.69 | 0.93 | 70.25 |
144.98 | 10.32 | 2.33 | 1.70 | 1.36 | 1.28 | 1.30 | 56.45 | 144.98 |
Table IV
Percent Standard Deviation of the Reflectance (Three Measurements at Each Position, 676.4-nm Data); 1-mm Grid Spacing
0.22 | 0.12 | 0.23 | 0.19 | 0.07 | 0.05 | 0.17 | 0.12 | 0.00 |
0.08 | 0.12 | 0.09 | 0.05 | 0.04 | 0.10 | 0.11 | 0.08 | 0.09 |
0.00 | 0.07 | 0.08 | 0.11 | 0.14 | 0.11 | 0.07 | 0.11 | 0.06 |
0.11 | 0.09 | 0.10 | 0.08 | 0.12 | 0.00 | 0.03 | 0.09 | 0.07 |
0.07 | 0.10 | 0.03 | 0.06 | 0.12 | 0.10 | 0.12 | 0.07 | 0.04 |
0.06 | 0.08 | 0.06 | 0.06 | 0.10 | 0.11 | 0.05 | 0.04 | 0.07 |
0.03 | 0.03 | 0.03 | 0.00 | 0.05 | 0.01 | 0.02 | 0.05 | 0.05 |
0.00 | 0.04 | 0.07 | 0.02 | 0.02 | 0.04 | 0.01 | 0.08 | 0.17 |
0.00 | 0.99 | 0.01 | 0.02 | 0.04 | 0.06 | 0.05 | 0.12 | 0.00 |
Table V
d∊/∊, the Percent Change in Internal Quantum Efficiency at 676.4 nm of DR11 with Respect to Position Relative to Central Datum Point; 1-mm Grid Spacing
−0.03 | 0.00 | 0.00 | 0.03 | 0.03 | −0.05 | −0.01 |
−0.02 | −0.04 | 0.03 | 0.03 | 0.02 | 0.05 | 0.04 |
−0.02 | 0.00 | −0.02 | 0.03 | 0.04 | 0.05 | 0.05 |
−0.04 | −0.03 | −0.01 | 0.00 | 0.03 | 0.00 | 0.05 |
−0.13 | −0.03 | −0.04 | −0.01 | 0.01 | −0.43 | −0.02 |
−0.13 | −0.07 | −0.06 | −0.33 | −0.39 | −0.06 | −0.05 |
−0.16 | −0.10 | −0.11 | −0.10 | −0.06 | 0.00 | −0.03 |
Table VI
d∊/∊ of DR11 Repeated at 676.4 nm after Removal of Dust Spots; 1-mm Grid Spacing
−0.09 | −0.03 | −0.04 | −0.01 | 0.01 | −0.09 | −0.04 |
−0.02 | −0.03 | −0.02 | 0.02 | 0.02 | 0.03 | 0.02 |
−0.04 | 0.00 | −0.01 | 0.00 | 0.02 | 0.02 | 0.02 |
−0.08 | −0.02 | −0.02 | 0.00 | 0.05 | 0.02 | 0.00 |
−0.13 | −0.04 | −0.05 | −0.05 | 0.00 | 0.14 | 0.00 |
−0.17 | −0.08 | −0.03 | −0.33 | −0.02 | −0.01 | −0.05 |
−0.15 | −0.10 | −0.10 | −0.08 | −0.02 | 0.02 | −0.01 |
Table VII
d∊/∊, the Percent Change in Internal Quantum Efficiency at 406.7 nm of DR11 with Respect to Position Relative to Central Datum Point; 1-mm Grid Spacing
−0.15 | 0.14 | 0.04 | 0.27 | 0.17 | 0.13 | 0.13 |
−0.24 | −0.08 | 0.03 | 0.12 | 0.21 | 0.45 | 0.47 |
−0.33 | −0.25 | −0.21 | −0.01 | 0.21 | 0.09 | 0.50 |
−0.67 | −0.52 | −0.27 | 0.00 | 0.16 | 0.40 | 0.47 |
−0.97 | −0.74 | −0.53 | −0.12 | −0.06 | −0.26 | 0.28 |
−1.30 | −1.17 | −0.90 | −1.99 | −0.47 | −0.84 | −0.40 |
−1.48 | −1.28 | −1.20 | −0.79 | −0.65 | −0.27 | −0.86 |
Table VIII
Calculated d∊/∊ Percentage Minus Measured d∊/∊ Percentage for DR11 at 676.4 nm; 1-mm Grid Spacing
0.03 | 0.00 | 0.00 | −0.02 | −0.03 | 0.05 | 0.00 |
0.02 | 0.04 | −0.03 | −0.03 | −0.02 | −0.03 | −0.02 |
0.00 | 0.00 | 0.02 | −0.03 | −0.04 | −0.05 | −0.03 |
0.01 | 0.00 | 0.00 | 0.00 | −0.03 | 0.02 | −0.03 |
0.09 | 0.00 | 0.02 | 0.00 | 0.00 | 0.42 | 0.03 |
0.08 | 0.02 | 0.02 | 0.25 | 0.37 | 0.03 | 0.03 |
0.10 | 0.05 | 0.06 | 0.07 | 0.03 | −0.01 | 0.00 |