Abstract
Broadband fluorescence enhancement in Cr-doped fibers (CDFs) fabricated by drawing-tower integrated powder-in-tube with redrawing technique is proposed and demonstrated. The CDFs after heat treatment exhibited Cr+4 emission enhancement with spectral density of 200 pW/nm which was identified as the formation of α-Mg2SiO4 nanocrystalline structures in the core, observed by HRTEM.
© 2013 Optical Society of America
PDF ArticleMore Like This
Yi-Chung Huang, Jau-Sheng Wang, Kuei-Ming Chu, Ting-Chien Lin, Wei-Lun Wang, Ta-Lung Chou, Szu-Ming Yeh, Sheng-Lung Huang, and Wood-Hi Cheng
OWS1 Optical Fiber Communication Conference (OFC) 2011
Yi-Chung Huang, Jau-Sheng Wang, Ting-Chien Lin, Yen-Sheng Lin, Wei-Lun Wang, Yu-Kuan Lu, Yun-Chung Lin, Szu-Ming Yeh, Hsin-Hui Kuo, Sheng-Lung Huang, and Wood-Hi Cheng
OMG5 Optical Fiber Communication Conference (OFC) 2010
Fang-Yen Lo, Chun-Nien Liu, Yi-Chung Huang, Wei-Lun Wang, Yen-Sheng Lin, Ta-Lung Chou, PiLing Huang, Sheng-Lung Huang, and Wood-Hi Cheng
WS3_2 OptoElectronics and Communications Conference and Photonics in Switching (OECC) 2013