Abstract
For the first time, based on the high crystalline quality of n-GaN on Si template, highly efficient InGaN/GaN LEDs grown on 4-inch silicon substrates comparable to those on sapphire substrates have been successfully demonstrated. At driving current of 350 mA, the overall output power of 1×1 mm2 LED chips exceeded 420 mW and forward voltage was 3.2 V under un-encapsulated condition, which is the best value among the reported values of blue LED grown on Si substrates. The internal quantum efficiency of 76% at injection current of 350 mA was measured.
© 2011 Optical Society of America
PDF ArticleMore Like This
Chien-Chung Lin, Ching-Hsueh Chiu, H. W. Huang, Shih-Pang Chang, Hao-Chung Kuo, and Chun-Yen Chang
83120C Asia Communications and Photonics Conference and Exhibition (ACP) 2011
H. P. T. Nguyen, S. Zhang, K. Cui, X. Han, and Z. Mi
CMU4 CLEO: Science and Innovations (CLEO:S&I) 2011
C. H. Chiu, D. W. Lin, C. C. Lin, Z. Y. Li, H. C. Kuo, T. C. Lu, S. C. Wang, W. T. Liao, T. Tanikawa, Y. Honda, M. Yamaguchi, and N. Sawaki
JWA94 CLEO: Applications and Technology (CLEO:A&T) 2011