Nearly stoichiometric LiTaO3 (SLT) crystals exhibited a high photorefractive damage resistance along with a negligibly small green-induced infrared absorption, even without the addition of MgO dopants. A bulk periodically poled device was successfully fabricated using a 3 mm-thick SLT crystal.